反應等離子噴涂制備原位TiC顆粒增強Fe基金屬陶瓷涂層

張守全; 朱警雷; 王海濤; 黃繼華; 張華; 趙興科

doi:10.13374/j.issn1001-053x.2009.03.029

留言板

尊敬的讀者、作者、審稿人, 關于本刊的投稿、審稿、編輯和出版的任何問題, 您可以本頁添加留言。我們將盡快給您答復。謝謝您的支持!

姓名

郵箱

手機號碼

標題

留言內容

驗證碼

反應等離子噴涂制備原位TiC顆粒增強Fe基金屬陶瓷涂層

doi: 10.13374/j.issn1001-053x.2009.03.029

1. 北京科技大學材料科學與工程學院, 北京 100083;
2. 廈門金鷺特種合金有限公司合金部, 廈門 361006

基金項目:

焊接國家重點實驗室開放資助項目

河南杰出人才創新基金資助項目(No.0421001000)

詳細信息

作者簡介:
張守全(1970-),男,博士研究生;黃繼華(1961-),男,教授,博士生導師,E-mail:jihuahuang47@sina.com

中圖分類號: TB333;TG174.443
計量
- 文章訪問數: 124
- HTML全文瀏覽量: 32
- PDF下載量: 6
- 被引次數: 0
出版歷程
- 收稿日期: 2008-03-31
- 網絡出版日期: 2021-08-09

TiC-reinforced Fe-base metal ceramic composite coatings fabricated by reactive plasma spraying

1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China;
2. Xiamen Golden Egret Special Alloy Co. Ltd., Xiamen 361006, China

摘要

摘要: 以鈦鐵粉、鐵粉和蔗糖(碳的前驅體)為原料,采用前驅體熱分解復合技術制備了Fe-Ti-C系反應熱噴涂粉末,并通過普通等離子噴涂技術原位合成并沉積了TiC/Fe金屬陶瓷復合涂層.利用XRD、SEM和EDS研究了噴涂粉末和復合涂層的相組成和顯微結構.結果表明:前驅體熱分解復合技術制備的Fe-Ti-C反應噴涂粉末粒徑均勻,原料粉末顆粒間的結合強度高;所制備的TiC/Fe復合涂層主要由不同含量TiC顆粒分布于金屬Fe基體內部而形成的復合片層疊加而成;TiC顆粒大致呈球形,粒徑呈納米級;TiC理論質量分數53%的TiC/Fe金屬陶瓷涂層的耐磨粒磨損性能較好,SRV磨損實驗中涂層的磨損面積為基體(45鋼)的1/25左右.
- 復合涂層 /
- 金屬陶瓷涂層 /
- 反應等離子噴涂 /
- 前驅體 /
- 蔗糖
Abstract: A kind of Fe-Ti-C composite powder for reactive spraying was prepared with ferrotitanium and sucrose as raw materials. TiC/Fe composite coatings were synthesized and deposited by reactive plasma spraying (RPS). XRD, SEM and EDS were employed to analyze the composition and microstructure of the composite powder and coatings. The wear resistance properties of the coatings were also tested. The results show that the particles of Fe-Ti-C composite powder for RPS are uniform without any impurity and the bonding strength among the raw material particles is strong. TiC/Fe composite coatings by RPS are composed of layers in which round TiC particles are dispersed within the Fe-alloy matrix. The size of round TiC particles is mostly less than 0.5 μm. The wearing capacity of TiC/Fe composite coatings with 53 % TiC is 25 times that of the substrate (45 steel) in a SRV tester.
- composite coatings /
- cermet coating /
- reactive plasma spray /
- precursor /
- sucrose