TiO₂對連鑄保護渣非等溫結晶過程的影響

doi: 10.13374/j.issn1001-053x.2010.03.006

冀成慶^1,2,
謝兵^1,2,
雷云^1,2,
刁江^1,2,
齊飛³

1. 重慶大學材料科學與工程學院, 重慶 400044;
2. 重慶大學重慶市冶金工程重點實驗室, 重慶 400044;
3. 中冶京誠工程技術有限公司, 北京 100176

基金項目:

國家自然科學基金資助項目(No.50474024)

教育部博士點基金資助項目(No.200806110006)

詳細信息

作者簡介:
冀成慶(1985-),男,碩士研究生;謝兵(1957-),教授,博士生導師,E-mail:bingxie@cqu.edu.cn

中圖分類號: TF777.1
計量
- 文章訪問數: 227
- HTML全文瀏覽量: 94
- PDF下載量: 6
- 被引次數: 0
出版歷程
- 收稿日期: 2009-07-20

Effects of TiO₂ on nonisothermal crystallization process of casting mold fluxes

JI Cheng-qing^1,2,
XIE Bing^1,2,
LEI Yun^1,2,
DIAO Jiang^1,2,
QI Fei³

1. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China;
2. Chongqing Key Laboratory of Metallurgical Engineering, Chongqing University, Chongqing 400044, China;
3. CERI Engineering Technology Co., Ltd., Beijing 100176, China

摘要

摘要: 采用熱絲法、X射線衍射(XRD)以及礦相方法研究TiO₂對保護渣非等溫結晶過程的影響.結果表明:槍晶石是含鈦保護渣的主要物相.在綜合堿度為1.3的基礎渣中加入質量分數2%～8%TiO₂后,隨著TiO₂的加入,渣樣開始析出了少量的Ca₂SiO₄、Ca₂Al(AlSi₇O₇)、Ca₂SiO₂F₂和CaTiO₃晶體.雖然加入TiO₂,促進了析晶種類的增加,但保護渣的結晶過程的時間延長,且保護渣的結晶速率和結晶率降低.因此,加入TiO₂后,抑制了保護渣的析晶,從而保證在控制渣膜熱流的前提下,提高玻璃態的比例以改善潤滑.
- 保護渣 /
- 結晶 /
- 非等溫 /
- 連鑄
Abstract: The nonisothermal crystallization behavior of mold fluxes bearing various TiO₂ was studied by using the single hot thermocouple technique.The mineral components of the mold fluxes were analyzed by X-ray diffraction (XRD) and microscopically observed by mine-phase microscope.The results indicate that cuspidine is the main phase of the casting mold fluxes.With a certain amount of TiO₂ (2% to 8%) added into the mold fluxes at high basicity (ΣR=1.3),the phase precipitation increases.Small amount of Ca₂SiO₄,Ca₂Al(AlSi₇O₇),Ca₂SiO₂F₂ and CaTiO₃ are crystallized.While the time of crystallization process of the mold fluxes is lengthened,the crystallization ratio and crystallization rate of the mold fluxes is decreased.Thus,crystallization of the mold fluxes is inhibited,leading to improvement in the glass property and the lubrication between casting strands and molds in view of the heat flow control of slag films.
- mold fluxes /
- crystallization /
- nonisothermal /
- casting