Si3N4 particle-reinforced 316L stainless steel prepared by powder injection molding
-
摘要: 以多組元水溶性黏結劑為黏結劑,采用粉末注射成形工藝成功制備出了Si3N4顆粒增強316L不銹鋼復合材料.研究表明:以聚乙二醇(PEG)、聚乙烯醇縮丁醛(PVB)和硬脂酸(SA)為主要成分的水溶性黏結劑表現出較好的水溶脫脂性能,注射坯在蒸餾水中脫脂6 h后,黏結劑總脫除率約為55%,其中PEG的脫除率約為78.6%;復合材料經燒結后組織均勻致密,性能良好,其致密度、硬度和拉伸強度分別為97.5%、HRB 81.7和620 MPa,其硬度和拉伸強度分別比采用石蠟基黏結劑制備的PIM-Si3N4增強316L不銹鋼復合材料提高5%和20.4%.Abstract: Si3N4 particle-reinforced 316L stainless steel composites were prepared by powder injection molding(PIM) using water-soluble binders.It is shown that a water-soluble binder mainly consisting of polyoxymethylene(PEG),polyvinyl butyral(PVB) and stearic acid(SA) exhibits a better water-soluble degreasing performance.After degreasing injection parts in water for 6 h,the total binder removal rate is 55% and the PEG removal rate is 78.6%.The sintered composites have a uniform microstructure and excellent properties with a relative density of 95.2%,a hardness of HRB 79.8 and a tensile strength of 620 MPa.And the hardness and tensile strength are 5% and 20.4% higher than the Si3N4 particle-reinforced 316L stainless steel produced by PIM with a paraffin wax-based binder,respectively.
-
點擊查看大圖
計量
- 文章訪問數: 133
- HTML全文瀏覽量: 27
- PDF下載量: 6
- 被引次數: 0
下載: