冶煉關鍵參數對于IF鋼軋材夾雜缺陷的影響

郝陽; 包燕平; 李任春; 李太全; 程迪; 陳霄; 王睿

doi:10.13374/j.issn2095-9389.2017.03.008

冶煉關鍵參數對于IF鋼軋材夾雜缺陷的影響

doi: 10.13374/j.issn2095-9389.2017.03.008

郝陽¹,
包燕平^1, ,,
李任春²,
李太全²,
程迪²,
陳霄¹,
王睿¹

1) 北京科技大學鋼鐵冶金新技術國家重點實驗室, 北京 100083
2) 邯鄲鋼鐵集團有限責任公司, 邯鄲 056015

基金項目:

“十二五”科技支撐計劃資助項目（2015BAF30B01）；教育部博士點專項基金資助項目（20130006110023）；鋼鐵冶金新技術國家重點實驗室自主基金資助項目（41614014）

詳細信息

中圖分類號: TF703.54
計量
- 文章訪問數: 820
- HTML全文瀏覽量: 256
- PDF下載量: 17
- 被引次數: 0
出版歷程
- 收稿日期: 2016-05-23

Influence of key parameters in steelmaking progress on the inclusion defects of rolled IF steel sheet

1) State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China
2) Handan Iron Steel Group Co. Ltd, Handan 056015, China

摘要

摘要: 針對邯鋼IF鋼冶煉過程，采用統計學軟件SPSS中邏輯回歸分析、相關性統計、描述性統計等方法，研究了冶煉過程中關鍵參數和軋材夾雜缺陷之間的對應關系以及參數間的相關性.結果表明：在IF鋼冶煉過程中將轉爐終點溫度控制在1695~1700℃之間，吹氧量控制在250 m³以下，靜置時間控制在30~40 min之間，加鋁前氧位不超過3.9×10^-4時，IF鋼軋材出現夾雜缺陷的機率減少.由此對現場提出了改善措施，結果表明以上優化措施可以減少IF鋼軋材中夾雜缺陷的產生.
- 煉鋼 /
- IF鋼 /
- 夾雜 /
- 統計 /
- 相關性
Abstract: Aiming at the steelmaking process of IF steel in Han-Steel, the relationship between key parameters and the defects of the rolled sheet was investigated, and the correlation among the parameters was also analyzed through the logic regression analysis, correlation statistics, descriptive statistics and other methods in the statistical software SPSS. The results show that the probability of inclusion defects in the rolled sheet reduces in the steelmaking process of IF steel when the end-point temperature of BOF is controlled in the range of 1695-1700℃, the oxygen blow amount below 250 m³, the holding time in the range of 30-40 min and the oxygen content before adding aluminum below 3. 9×10^-4. Besides, the improvement measures were carried out and the results show that the optimization measures can reduce the inclusion defects of rolled IF steel sheet.
- steelmaking /
- IF steel /
- inclusions /
- statistics /
- correlation

HTML全文

參考文獻(4)

[2]	Cui H, Wu H J, Yue F, et al. Surface defects of cold-rolled Ti-IF steel sheets due to non-metallic inclusions. J Iron Steel Res Int, 2011, 18(Suppl 2):335
[9]	Miyake T, Morishita M, Nakata H, et al. Influence of sulphur content and molten steel flow on entrapment of bubbles to solid/liquid interface. ISIJ Int, 2006, 46(12):1817
[10]	Yu H X, Ji C X, Chen B, et al. Characteristics and evolution of inclusion induced surface defects of cold rolled IF sheet. J Iron Steel Res Int, 2015, 22(Suppl 1):17
[11]	Chen Y, Zeng J H, Wu G R. Control for surface faint-sliver defects in cold-rolled IF steel sheet. Adv Mater Res, 2011, 396-398:1145