摘要: 碘化鉛是有機無機雜化鈣鈦礦太陽能電池的關鍵原料, 其使用方法為溶解在二甲基甲酰胺(DMF)中然后制成膜.碘化鉛在DMF中的溶解性對電池器件的性能有重要影響.本文經實驗判斷, 造成碘化鉛在DMF中溶解性差的原因是H2O、PbO、PbO2等氧化物在碘化鉛晶體表面形成氧化物薄膜, 阻礙其溶解.在一定范圍內, 碘化鉛在DMF中溶解性取決于碘化鉛合成過程中反應溶液的pH值.經過掃描電鏡、X射線衍射、X射線光電子能譜等分析檢測, 確定有機無機雜化鈣鈦礦太陽能電池用碘化鉛最佳合成pH值為2;且在一定范圍內反應溶液pH值、滴速和溶液濃度不會影響碘化鉛的微觀形貌及其在DMF中的溶解性; 同時發現重結晶、熱反應以及慢滴速反應條件會使碘化鉛樣品在(001)面擇優生長.Abstract: Solar energy is an ideal renewable energy, and how to use solar energy efficiently is a hot topic for many researchers. So far, the development of solar cells has gone through three generations. The first generation used crystalline silicon cells; the second generation used thin-filmsolar cells. At present, the third generation utilizes new-type solar cells. As a part of the third-generation solar cells, perovskite solar cells have developed rapidly in recent years, making thema subject of a very vital research area. Lead iodide is a key raw material for organic-inorganic hybrid perovskite solar cells, and it is used by dissolving in dimethylformamide(DMF), thereby forming a film. Experimental results show that the reason for poor solubility of lead iodide in DMF is that oxides, such as H2O, PbO, and PbO2, tend to formoxide films on the surface of lead iodide crystals, which hinder its dissolution. Within a certain range, the solubility of lead iodide in DMF depends on the pH of the reaction solution during the synthesis process. After performing scanning electron microscope, X-ray diffraction, X-ray photoelectron spectroscopy and other analytical tests, the optimal synthesis pH of lead iodide for the organic-inorganic hybrid perovskite solar cells is 2. Within a certain range, the pH value, dropping speed, and solution concentration of the reaction solution do not affect the microscopic morphology of lead iodide and its solubility in DMF. Simultaneously, results indicate that the recrystallization, thermal reaction, and low dropping speed reaction conditions led to the preferential growth of lead iodide on the(001)surface.
-
Key words:
- perovskite solar cells /
- lead iodide /
- dimethylformamide /
- solubility /
- preparation process
-
圖 2 試樣1~14(001)晶面衍射峰強度對比圖
Figure 2. (001)crystal plane diffraction peak intensity comparison of Samples 1-14
圖 5 試樣1~4和試樣14的X射線光電子能譜中O 1s分峰擬合圖譜
Figure 5. XPS O1s sub-peak fitting maps of Samples 1-4 and 14
中文字幕在线观看
圖 8 試樣1~14制備的鈣鈦礦太陽能電池平均轉換效率
Figure 8. Average efficiency of perovskite solar cells prepared with Samples 1-14
-
參考文獻
[1] Mei H L, Tang L D, Wang B, et al. Recent progress of perovskite solar cells. J Liaoning Univ Technol Nat Sci Ed, 2016, 36(1): 48 https://www.cnki.com.cn/Article/CJFDTOTAL-LNGX201601013.htm梅海林, 唐立丹, 王冰, 等. 鈣鈦礦型太陽能電池的研究進展. 遼寧工業大學學報(自然科學版), 2016, 36(1): 48 https://www.cnki.com.cn/Article/CJFDTOTAL-LNGX201601013.htm [2] Green M A. Third generation photovoltaics: advanced solar energy conversion. Phys Today, 2004, 57(12): 71 doi: 10.1063/1.1878345 [3] Rakitin V V, Novikov G F. Third-generation solar cells based on quaternary copper compounds with the kesterite-type structure. Russ ChemRev, 2017, 86(2): 99 [4] Jung H S, Park N G. Perovskite solar cells: frommaterials to devices. Small, 2014, 11(1): 10 http://www.ncbi.nlm.nih.gov/pubmed/25358818 [5] Park N G. Perovskite solar cells: an emerging photovoltaic technology. Mater Today, 2015, 18(2): 65 doi: 10.1016/j.mattod.2014.07.007 [6] Song Z N, Watthage S C, Phillips A B, et al. Pathways toward high-performance perovskite solar cells: review of recent advances in organo-metal halide perovskites for photovoltaic applications. J Photon Energy, 2016, 6(2): 022001 doi: 10.1117/1.JPE.6.022001 [7] Green M A, Ho-Baillie A, Snaith H J. The emergence of perovskite solar cells. Nature Photon, 2014, 8(7): 506 doi: 10.1038/nphoton.2014.134 [8] Snaith H J. Perovskites: the emergence of a new era for low-cost, high-efficiency solar cells. J Phys ChemLett, 2013, 4(21): 3623 [9] Green M A, Ho-Baillie A. Perovskite solar cells: the birth of a new era in photovoltaics. ACS Energy Lett, 2017, 2(4): 822 doi: 10.1021/acsenergylett.7b00137 [10] Zhu X H.Studies on Polycrystalline Synthesis and Single Crystal Growth of LeadIodide[Dissertation].Chengdu: Sichuan University, 2006朱興華. 碘化鉛多晶合成與單晶生長研究[學位論文]. 成都: 四川大學, 2006 [11] O'Regan B C, Barnes P R F, Li X E, et al. Optoelectronic studies of methylammoniumlead iodide perovskite solar cells with mesoporous TiO2: separation of electronic and chemical charge storage, understanding two recombination lifetimes, and the evolution of band offsets during J-V hysteresis. J AmChemSoc, 2015, 137(15): 5087 doi: 10.1021/jacs.5b00761 [12] Deng H, Dong D D, Qiao K K, et al. Growth, patterning and alignment of organolead iodide perovskite nanowires for optoelectronic devices. Nanoscale, 2015, 7(9): 4163 doi: 10.1039/C4NR06982J [13] Hao F, Stoumpos C C, Cao D H, et al. Lead-free solid-state organic-inorganic halide perovskite solar cells. Nature Photon, 2014, 8: 489 doi: 10.1038/nphoton.2014.82 [14] Hendon C H, Yang R X, Burton L A, et al. Assessment of polyanion(BF4－ and PF6－)substitutions in hybrid halide perovskites. J Mater ChemA, 2014, 3(17): 9067 http://pubs.rsc.org/en/content/articlehtml/2015/ta/c4ta05284f [15] KimH S, Lee C R, ImJ H, et al. Lead iodide perovskite sensitized all-solid-state submicron thin filmmesoscopic solar cell with efficiency exceeding 9%. Sci Rep, 2012, 2(8): 591 http://www.ncbi.nlm.nih.gov/pmc/articles/PMC3423636/ [16] David D C, James R B, Feemster H, et al. Investigation of lead iodide crystals for use as high energy solid state radiation detectors. MRS Online Proc Library Archive, 1993, 302: 335 doi: 10.1557/PROC-302-335 [17] Liu J, Zhang Y. Effect of temperature gradient on the growth of PbI2crystal for nuclear radiation detectors. Bull Chin CeramSoc, 2016, 35(11): 3893 https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201611069.htm劉靜, 張羽. 溫度梯度對核輻射探測器用PbI2晶體生長影響研究. 硅酸鹽通報, 2016, 35(11): 3893 https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201611069.htm [18] Li X H, Zhu X H, Sun H, et al. Radiation detector based on lead iodide(PbI2). Electron Sci Technol, 2017, 30(5): 69 doi: 10.3969/j.issn.1001-2400.2017.05.012李小輝, 朱興華, 孫輝, 等. 基于碘化鉛X射線室溫輻射探測器的研究. 電子科技, 2017, 30(5): 69 doi: 10.3969/j.issn.1001-2400.2017.05.012 [19] Zhao X. Research development of PbI2single crystal growth and room-temperature nuclear radiation detectors. Mater Rev, 2011, 25(1): 80 https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201101018.htm趙欣. 碘化鉛單晶生長及探測器的研究進展. 材料導報, 2011, 25(1): 80 https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201101018.htm [20] Yang D Y, Zhu X H, Sun H, et al. Structural, morphological and optical properties of PbI2 thick film. Spectrosc Spectr Anal, 2014, 34(11): 2892 doi: 10.3964/j.issn.1000-0593(2014)11-2892-05楊定宇, 朱興華, 孫輝, 等. PbI2 厚膜的結構、形貌與光譜性質研究. 光譜學與光譜分析, 2014, 34(11): 2892 doi: 10.3964/j.issn.1000-0593(2014)11-2892-05 [21] Jin Y R, Li L X, He Y, et al. Growth of PbI2 single crystal with ascending U type ampoule. J Xihua Univ Nat Sci, 2007, 26(1): 31 https://www.cnki.com.cn/Article/CJFDTOTAL-SCGX200701009.htm金應榮, 李麗霞, 賀毅, 等. U型坩堝上升法生長碘化鉛單晶體. 西華大學學報(自然科學版), 2007, 26(1): 31 https://www.cnki.com.cn/Article/CJFDTOTAL-SCGX200701009.htm [22] Sun H, Zhu X H, Yang D Y, et al. Electrical and γ-ray energy spectrumresponse properties of PbI2 crystal grown by physical vapor transport. J Semicond, 2012, 33(5): 053002-1 doi: 10.1088/1674-4926/33/5/053002 [23] Hommerich U, Brown E, Trivedi S B, et al. Synthesis and 1.5 μmemission properties of Nd3+ activated lead bromide and lead iodide crystals[J]. Appl Phys Lett, 2006, 88(25): 1906 doi: 10.1063/1.2216420 [24] Wang B.A Method for Growing Single Crystals of LeadIodide: China Paten, CN106012013A. 2016-10-12王冰. 一種生長碘化鉛單晶體的方法: 中國專利, CN106012013A. 2016-10-12 [25] Wangyang P H, Sun H, Zhu X H, et al. Mechanical exfoliation and Raman spectra of ultrathin PbI2 single crystal. Mater Lett, 2016, 168: 68 doi: 10.1016/j.matlet.2016.01.034 [26] Chen Y H, Li L, Liu Z H, et al. Photon management for efficient hybrid perovskite solar cells via synergetic localized grating and enhanced fluorescence effect. Nano Energy, 2017, 40: 540 doi: 10.1016/j.nanoen.2017.08.059 -
下載:
點擊查看大圖
圖(8)
計量
- 文章訪問數: 1686
- HTML全文瀏覽量: 622
- PDF下載量: 151
- 被引次數: 0