摘要: 采用水熱法制備Zn?In LDHs，并且將其作為鋅鎳二次電池的新型負極材料。利用掃描電鏡（SEM）和X射線衍射儀（XRD）對制備的Zn?In LDHs進行了形態和微觀結構的分析。通過循環伏安（CV）、Tafel極化曲線和恒電流充電放電測試研究了Zn?In LDHs作為鋅鎳電池負極材料的電化學性能。形貌表征發現制備的Zn?In LDHs呈現出六邊形片狀結構，電化學性能研究結果表明Zn?In LDHs應用到Zn–Ni二次電池中具有很好的循環可逆性能和抗腐蝕性能，恒電流充電放電測試結果分析可知，Zn?In LDHs電極表現出了較為優異的循環穩定性以及充放電特性。經過100次循環后，循環保持率可以達到92.25%。Abstract: Although zinc–nickel (Zn–Ni) secondary batteries have numerous advantages, these have not been widely used in practice. The main reason is that problems such as the formation of dendritic zinc, corrosion, and passivation are encountered in the use of zinc anode. These problems restrict the development of Zn–Ni secondary battery using zinc electrode. To improve the electrochemical properties of zinc anode, researchers are constantly looking for new materials to be applied to Zn–Ni secondary batteries. Recently, many studies on the modification of zinc oxide and the electrochemical properties of calcium zincate have been conducted. The improvement measures can effectively enhance the corrosion resistance and cycle stability of Zn–Ni secondary batteries, but the improvements are not up to expectations. Therefore, researchers have now focused their attention on the research and development of new materials. The unique properties of hydrotalcite have attracted the attention of researchers. Hydrotalcite has shown excellent performance in electrocatalysis, medicine, nanofillers, and other functional fields. Moreover, because hydrotalcite has high stability in alkaline solution, hydrotalcite may become a new material for alkaline batteries. Presently, hydrotalcite, as a new kind of B-type material, has been used in alkaline secondary batteries; the performance of these batteries is excellent. The introduction of Zn–Al LDHs effectively improves the electrochemical properties of Zn–Ni secondary batteries. Therefore, this study proposes the application of Zn–In LDHs to Zn–Ni secondary batteries for the first time to analyze its electrochemical properties. Zn–In LDHs were prepared via the hydrothermal method and used as a new anode material for Zn–Ni secondary batteries. The morphology and microstructure of Zn–In LDHs were analyzed via scanning electron microscopy and X-ray diffraction, respectively. The electrochemical properties of Zn–In LDHs as anode material for Zn–Ni batteries were investigated via cyclic voltammetry, Tafel extrapolation of polarization curves, and galvanostatic charge–discharge test. The morphology of Zn–In LDHs shows a hexagonal structure. The electrical properties of Zn–In LDHs show that they have good cycle reversibility and corrosion resistance when Zn–In LDHs are applied to Zn–Ni secondary batteries. The analysis of the constant current charge–discharge test results shows that Zn–In LDHs have excellent cycle stability and charge–discharge characteristics. After 100 cycles, the cycle retention rate can reach values of up to 92.25%.
-
圖 4 ZnO、Zn–Al LDHs、Zn?In LDHs電極的循環伏安曲線
Figure 4. Cyclic voltammetry curves of ZnO, Zn–Al LDHs, and Zn–In LDH electrodes
圖 5 ZnO、Zn–Al LDHs、Zn?In LDHs電極的Tafel曲線
Figure 5. Tafel curves of ZnO, Zn–Al LDH, and Zn–In LDH electrodes
圖 7 鋅電極第50次充放電特性曲線
Figure 7. The 50th charge and discharge characteristic curves of zinc electrode
中文字幕在线观看表 1 ZnO、Zn–Al LDHs、Zn?In LDHs電極的Tafel曲線數據
Table 1. Tafel curve data of ZnO, Zn–Al LDHs, and Zn–In LDHs electrodes
Sample Ecorr/V jcorr/(A·cm?2) ZnO ?1.432 0.489 Zn–Al LDHs ?1.419 0.391 Zn–In LDHs ?1.374 0.218 
下載: 導出CSV
-
參考文獻
[1] Guo B K, Li X H, Yang S Q. Principle and Manufacturing Technology of Chemical Power Battery. Changsha: Central South University Press, 2009郭炳焜, 李新海, 楊松青. 化學電源: 電池原理及制造技術. 長沙: 中南大學出版社, 2009 [2] He H M, Yang Z H, Chi W W, et al. The performance of indium oxide coated zinc oxide for Zn?Ni battery. Battery Bimonthly, 2011, 41(2): 101 doi: 10.3969/j.issn.1001-1579.2011.02.014賀紅梅, 楊占紅, 遲偉偉, 等. 鋅鎳電池用包覆氧化銦的氧化鋅的性能. 電池, 2011, 41(2):101 doi: 10.3969/j.issn.1001-1579.2011.02.014 [3] Yuan Y F, Tu J P, Guo S Y, et al. Characteristics and electrochemical performance of Ni-coated ZnO prepared by an electroless plating proces. Appl Surf Sci, 2008, 254(16): 5080 doi: 10.1016/j.apsusc.2008.02.040 [4] Zhu L Q, Zhang H, Li W P, et al. Investigation of zinc powder modified by ultrasonic impregnation of rare earth lanthanum. Appl Surf Sci, 2007, 253(24): 9443 doi: 10.1016/j.apsusc.2007.06.008 [5] Yuan Y F, Tu J P, Wu H M, et al. Influence of surface modification with Sn6O4(OH)4 on electrochemical performance of ZnO in Zn/Ni secondary cells. J Power Sources, 2007, 165(2): 905 doi: 10.1016/j.jpowsour.2006.12.037 [6] Wu J Z, Tu J P, Yuan Y F, et al. Ag-modification improving the electrochemical performance of ZnO anode for Ni/Zn secondary batteries. J Alloys Compd, 2009, 479(1-2): 624 doi: 10.1016/j.jallcom.2009.01.013 [7] Zeng D Q, Yang Z H, Wang S W, et al. Preparation and electrochemical performance of In-doped ZnO as anode material for Ni–Zn secondary cells. Electrochim Acta, 2011, 56(11): 4075 doi: 10.1016/j.electacta.2011.01.119 [8] Yu S L, Yu X H, Lü X, et al. Sn6O4(OH)4 coated on ZnO surface: preparation and application in zinc-nickel secondary battery. J Inorg Chem, 2018, 33(9): 1573俞雙林, 俞小花, 呂祥, 等. 氧化鋅表面包覆Sn6O4(OH)4的制備及其在鋅鎳電池中的應用. 無機化學學報, 2018, 33(9):1573 [9] Wen R J, Yang Z H, Fan X M, et al. Electrochemical performances of ZnO with different morphology as anodic materials for Ni/Zn secondary batteries. Electrochim Acta, 2012, 83: 376 doi: 10.1016/j.electacta.2012.08.034 [10] Luo Z G, Sang S B, Wu Q M, et al. A conductive additive for Zn electrodes in secondary Ni/Zn batteries: The magneli phase titanium sub-oxides conductive ceramic TinO2n?1. ECS Electrochem Lett, 2012, 2(2): A21 doi: 10.1149/2.008302eel [11] Long W, Yang Z H, Liao Q F. The application of ZnO coated with carbon for Ni?Zn secondary battery. Appl Chem Ind, 2013, 42(6): 983龍偉, 楊占紅, 廖慶豐. 碳包覆氧化鋅材料在鋅鎳二次電池中的應用研究. 應用化工, 2013, 42(6):983 [12] Yu S L, Yu X H, Lü X, et al. Study on problems and solutions of zinc electrode for zinc-nickel battery. Chin J Power Sources, 2018, 42(10): 1585 doi: 10.3969/j.issn.1002-087X.2018.10.049俞雙林, 俞小花, 呂祥, 等. 鋅鎳電池負極存在的問題及解決途徑的研究. 電源技術, 2018, 42(10):1585 doi: 10.3969/j.issn.1002-087X.2018.10.049 [13] Shi X J, Wang Y H, Zhang Z S. Research progress in calcium zincate material for Zn–Ni secondary battery. Chin Labat Man, 2019, 56(3): 114施學金, 汪云華, 張戰勝. 鋅鎳二次電池用鋅酸鈣材料的研究進展. 蓄電池, 2019, 56(3):114 [14] Li Y G, Yu S L, Yu X H, et al. Preparation of calcium zincate with different morphologies and their applications in Zn–Ni battery. Mod Chem Ind, 2018, 38(5): 81李永剛, 俞雙林, 俞小花, 等. 不同形貌鋅酸鈣的制備及其在鋅鎳電池中的應用研究. 現代化工, 2018, 38(5):81 [15] Xu J, Pan Y M, Chen Q, et al. Research progress of preparation and applications of layered double hydroxides. China Plast, 2016, 30(4): 23徐堅, 潘玉妹, 陳強, 等. 水滑石的制備及應用進展. 中國塑料, 2016, 30(4):23 [16] Debecker D P, Gaigneaux E M, Busca G. Exploring, tuning, and exploiting the basicity of hydrotalcites for applications in heterogeneous catalysis. Chemistry, 2009, 15(16): 3920 doi: 10.1002/chem.200900060 [17] Mokhtar M, Saleh T S, Basahel S N. Mg–Al hydrotalcites as efficient catalysts for aza-Michael addition reaction: A green protocol. J Mol Catal A Chem, 2012, 353-354: 122 doi: 10.1016/j.molcata.2011.11.015 [18] Fan X M, Yang Z H, Long W, et al. The preparation and electrochemical performance of In(OH)3-coated Zn?Al?hydrotalcite as anode material for Zn–Ni secondary cell. Electrochim Acta, 2013, 92: 365 doi: 10.1016/j.electacta.2013.01.035 [19] Fan X M, Yang Z H, Wen R J, et al. The application of Zn–Al?hydrotalcite as a novel anodic material for Ni–Zn secondary cells. J Power Sources, 2013, 224: 80 doi: 10.1016/j.jpowsour.2012.09.101 [20] Xie X E, Yang Z H, Feng Z B, et al. Electrochemical properties of ZnO added with Zn?Al?hydrotalcites as anode materials for Zinc/Nickel alkaline secondary batteries. Electrochim Acta, 2015, 154: 308 doi: 10.1016/j.electacta.2014.12.101 [21] Yang B, Yang Z H, Peng Z G, et al. Effect of silver additive on the electrochemical performance of ZnAl-layered double hydroxide as anode material for nickel-zinc rechargeable batteries. Electrochim Acta, 2014, 132: 83 doi: 10.1016/j.electacta.2014.03.126 [22] Fan X M, Yang Z H, Xie X E, et al. The electrochemical behaviors of Zn–Al–La?hydrotalcite in Zn–Ni secondary cells. J Power Sources, 2013, 241: 404 doi: 10.1016/j.jpowsour.2013.04.136 [23] Zhang Z, Yang Z H, Huang J H, et al. Enhancement of electrochemical performance with Zn?Al?Bi layered hydrotalcites as anode material for Zn/Ni secondary battery. Electrochim Acta, 2015, 155: 61 doi: 10.1016/j.electacta.2014.12.145 [24] Wang T T, Yang Z H, Yang B, et al. The electrochemical performances of Zn–Sn–Al?hydrotalcites in Zn–Ni secondary cells. J Power Sources, 2014, 257: 174 doi: 10.1016/j.jpowsour.2014.02.006 [25] Wang R J, Yang Z H. Synthesis and high cycle performance of Zn–Al–In?hydrotalcite as anode materials for Ni–Zn secondary batteries. RSC Adv, 2013, 3(43): 19924 doi: 10.1039/c3ra43045f -
點擊查看大圖
圖(7) / 表(1)
計量
- 文章訪問數: 2421
- HTML全文瀏覽量: 818
- PDF下載量: 38
- 被引次數: 0