Dearsenification of Hot Metal with CaC<sub>2</sub>-CaF<sub>2</sub> Slag

Zhu Yuankai; Dung Yuanchij; Peng Yuqing; Wei Shoukun

doi:10.13374/j.issn1001-053x.1986.02.010

Volume 8 Issue 2

Nov. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 1986 > 8(2): 103-112

Zhu Yuankai, Dung Yuanchij, Peng Yuqing, Wei Shoukun. Dearsenification of Hot Metal with CaC2-CaF2 Slag[J]. Chinese Journal of Engineering, 1986, 8(2): 103-112. doi: 10.13374/j.issn1001-053x.1986.02.010

Citation:

Zhu Yuankai, Dung Yuanchij, Peng Yuqing, Wei Shoukun. Dearsenification of Hot Metal with CaC₂-CaF₂ Slag[J]. Chinese Journal of Engineering, 1986, 8(2): 103-112. doi: 10.13374/j.issn1001-053x.1986.02.010

Citation:

PDF( 733 KB)

Dearsenification of Hot Metal with CaC₂-CaF₂ Slag

doi: 10.13374/j.issn1001-053x.1986.02.010

Received Date: 1985-10-19
Available Online: 2021-11-16

Abstract

Abstract

Dearsenification of hot metal was studied on the bench scale with CaC₂-CaF₂ slag. Experiments were carried out in the Molybdenum-wound furnace under Ar atmosphere in the graphite crucible. Effects of temperature, composition and amount of slag, the initial As content and the Si content of hot metal on the degree of dearsenification were investigated.
Thermodynamic analysis has shown that dearsenification in iron and steel melts is only accomplished under reducing conditions. It has been ascertained that it is impossible to carry out desulfurization, dephosphorization and dearsenifieation of hot metal with CaC₂-CaF₂ or CaO-CaF₂ slag simultaneously.