Quenching-tempering Process Effect on Microstructure and Properties of 590 MPa High Strength Thick Plate

Li Xuetong; Wang Youming; Xu Jianguo; Xue Guijun

doi:10.13374/j.issn1001-053x.1998.03.036

Volume 20 Issue 3

Aug. 2021

Turn off MathJax

Article Contents

Article Navigation > Chinese Journal of Engineering > 1998 > 20(3): 273-276

Li Xuetong, Wang Youming, Xu Jianguo, Xue Guijun. Quenching-tempering Process Effect on Microstructure and Properties of 590 MPa High Strength Thick Plate[J]. Chinese Journal of Engineering, 1998, 20(3): 273-276. doi: 10.13374/j.issn1001-053x.1998.03.036

Citation:

Li Xuetong, Wang Youming, Xu Jianguo, Xue Guijun. Quenching-tempering Process Effect on Microstructure and Properties of 590 MPa High Strength Thick Plate[J]. Chinese Journal of Engineering, 1998, 20(3): 273-276. doi: 10.13374/j.issn1001-053x.1998.03.036

Citation:

PDF( 493 KB)

Quenching-tempering Process Effect on Microstructure and Properties of 590 MPa High Strength Thick Plate

doi: 10.13374/j.issn1001-053x.1998.03.036

1. Material Science and Engineering School, UST Beijing, Beijing 100083, China;
2. Technology Center, An'shan Iron and Steel Co, An'Shan 114001

Received Date: 1997-06-25
Available Online: 2021-08-27

Abstract

Abstract

A new quenching-tempering technology system is gotten, in which the quenching temperature is about 910~920℃ and the tempering temperature is about 550~580℃. With using this technology, the mechanical properties of the 590 MPa high strength thick plate are better satisfaction for the using demand. The new technology system is available for the steel plate of different composition.